View article

The thermal and flammability properties of polyamide 6/clay (2 and 5% by mass fraction) nanocomposites were measured to determine their flame retardant (FR) performance. The gasification process of the nanocomposite samples at an external radiant flux of 50kW/m² in a nitrogen atmosphere was observed, and the residues collected at various sample mass losses were analyzed by thermogravimetric analysis, transmission electron microscopy, and X-ray diffraction to determine the content of the residue and to understand the FR mechanism of the nanocomposites. The analysis of the floccules of blackened residues shows that up to 80% by mass of the residues consists of clay particles and the remainder is thermally stable organic components with possible graphitic structure. Furthermore, clay particles are stacked in the carbonaceous floccule residues and the d-spacing of the clay platelets is in the range of 1 …