We prepared pure and samarium-doped ZnS (Sm_xZn_1−xS_1+0.5x) nanoparticles via hydrothermal process at 160 °C for 24 h. XRD analysis shows that the particles were well crystallized and corresponds to a cubic sphalerite phase. SEM and TEM images indicate that the sizes of the particles were in the range of 20–60 nm. The photocatalytic activity of Sm-doped ZnS nanoparticles was evaluated by monitoring the decolorization of Reactive Red 43 in aqueous solution under visible light irradiation. The color removal efficiency of Sm_0.04Zn_0.96S and pure ZnS was 95.1% and 28.7% after 120 min of treatment, respectively. Among the different amounts of dopant agent used, 4% Sm-doped ZnS nanoparticles indicated the highest decolorization. We found that the presence of inorganic ions such as Cl⁻, CO₃²⁻ and other radical scavengers such as buthanol and isopropyl alcohol reduced the decolorization efficiency.