In the present work, a systematic study on microwave properties of Ca_1-xBi_xMo_1-xV_xO₄ (0.2 ≤ x ≤ 0.5) solid solution ceramics synthesized by using the traditional solid-state reaction method was conducted. A scheelite structured solid solution was formed in the composition range 0.2 ≤ x ≤ 0.5. We successfully prepared a microwave dielectric ceramic Ca_0.66Bi_0.34Mo_0.66V_0.34O₄ with a temperature coefficient of resonant frequency (TCF) near to zero and a low sintering temperature by using (Bi, V) substituted (Ca, Mo) in CaMoO₄ to form a solid solution. The Ca_0.66Bi_0.34Mo_0.66V_0.34O₄ ceramic can be well sintered at only 870 °C and exhibits good microwave dielectric properties with a permittivity (ε_r) ˜21.9, a Qf ˜18,150 GHz (at 7.2 GHz) (Q = quality factor = 1/dielectric loss; f = resonant frequency), a TCF ˜ + 0.1 ppm/°C. The chemical compatibility with silver indicated that the Ca_0.66Bi₀ …