View article

An experimental study was undertaken to determine how several variables affect the size of gas bubbles formed at nozzles in liquid pig iron. The frequency of bubble formation was measured by an acoustic device, which could detect the vibrations produced by the bubble release. Accurate knowledge of the gas flow rate then enabled the calculation of bubble volumes. The use of large baths (60 Kg), melted by induction heating, permitted a wide range of experimental parameters: gas flow rate (0.5 to 1000 cc/s), outside nozzle diameter (0.64 to 5.1 cm), inside diameter (0.16 to 0.64 cm), chamber volume (23 to 2200 cc), nozzle depth (7.6 to 20 cm), surface tension (700 to 1500 dynes/cm) and nozzle orientation (up, down and sideways). The resulting bubble volumes were between 0.5 and 100 cc. The bubbles were found to form at the outer diameter of the nozzles due to the nonwettability of the nozzles …