An insight into the thermo-mechanical behaviours of AZ31B and Elektron 717 magnesium alloys under the hot stamping conditions was established. High-temperature tensile tests (i.e. 350–450 °C) at a strain rate of 0.1 to 5/s were conducted to examine the material viscoplastic behaviours. Additionally, microstructure characterizations were performed, using the electron backscatter diffraction (EBSD), on the deformed samples to capture the underlying deformation mechanisms. Dynamic recrystallization (DRX) and texture formation were observed during the deformation at high temperature in both alloys and are the primary factors that affect the viscoplastic behaviours. The yield stress of both alloys reduced with increasing temperatures and reducing strain rates. More importantly, the ductility of the samples increased with both the temperatures and the strain rates. The higher ductility at higher strain rates was …