A high performance intermediate temperature fuel cell (ITFC) with composite electrolyte composed of co-doped ceria Ce_0.8Gd_0.05Y_0.15O_1.9 (GYDC) and a binary carbonate-based (52mol% Li₂CO₃/48mol% Na₂CO₃), 1.2mm thick electrolyte layer has been developed. Co-doped Ce_0.8Gd_0.05Y_0.15O_1.9 was synthesized by a glycine–nitrate process and used as solid support matrix for the composite electrolyte. The conductivity of both composite electrolyte and GYDC supporting substrate were measured by AC impedance spectroscopy. It showed a sharp conductivity jump at about 500°C when the carbonates melted. Single cells with thick electrolyte layer were fabricated by a dry-pressing technique using NiO as anode and Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3−δ or lithiated NiO as cathode. The cell was tested at 450–550°C using hydrogen as the fuel and air as the oxidant. Excellent performance with high power density of …