Atomic scale control of the thickness of thin film makes atomic layer deposition highly advantageous in the preparation of high quality super-lattices. However, precisely controlling the film chemical stoichiometry is very challenging. In this study, we deposited SiO_x film with different stoichiometry by plasma enhanced atomic layer deposition. After reviewing various deposition parameters like temperature, precursor pulse time, and gas flow, the silicon dioxides of stoichiometric (SiO₂) and non-stoichiometric (SiO_1.8 and SiO_1.6) were successfully fabricated. X-ray photo-electron spectroscopy was first employed to analyze the element content and chemical bonding energy of these films. Then the morphology, structure, composition, and optical characteristics of SiO_x film were systematically studied through atomic force microscope, transmission electron microscopy, X-ray reflection, and spectroscopic ellipsometry. The experimental results indicate that both the mass density and refractive index of SiO_1.8 and SiO_1.6 are less than SiO₂ film. The energy band-gap is approved by spectroscopic ellipsometry data and X-ray photo-electron spectroscopy O 1s analysis. The results demonstrate that the energy band-gap decreases as the oxygen concentration decreases in SiO_x film. After we obtained the Si-rich silicon oxide film deposition, the SiO_1.6/SiO₂ super-lattices was fabricated and its photoluminescence (PL) property was characterized by PL spectra. The weak PL intensity gives us greater awareness that more research is needed in order to decrease the x of SiO_x film to a larger extent through further optimizing plasma-enhanced atomic layer …