Zinc oxide (ZnO) nanosheets (ZnO-NS) were prepared for the photoanode of a dye-sensitized solar cell (DSSC), first by directly growing layered hydroxide zinc carbonate (LHZC) on an FTO substrate using a chemical bath deposition (CBD) method and then by transforming the LHZC into ZnO through pyrolysis at 300 °C. A light-to-electricity conversion efficiency (η) of 6.06% was achieved for the DSSC with ZnO-NS as its photoanode, under 100 mW cm−2 illumination, and this (η) was found to be much higher than that of the DSSC with ZnO nanoparticles (ZnO-NP) as the photoanode (2.92%). The far superior performance of the DSSC with ZnO-NS is essentially attributed to (i) higher effective electron diffusion coefficient of ZnO-NS (3.59 × 10−3 cm2s−1) than that of ZnO-NP (1.12 × 10−3 cm2s−1), and to (ii) higher dye loading on ZnO-NS (2.66 × 10−7 mol cm−2) than that on ZnO-NP (1.99 × 10−7 mol cm−2); this …