The aim of this work was to investigate the effect of the calcination temperature on the textural properties, structure and acidity of niobium phosphate and the relationship between those properties and the catalytic activity for the continuous esterification reaction using oleic acid and ethanol. For this purpose, samples of niobium phosphate were prepared by calcination at 300, 350, 400, 450, 500 and 600 °C. Despite the good thermal stability presented by niobium phosphate, best results were achieved for samples pretreated at 300 °C, which presented higher acidity, surface area and catalytic activity. For this sample, the experimental conditions of temperature (from 220 to 290 °C), amount of catalyst (from 0 to 0.8 g) and ethanol:oleic acid molar ratio (from 2:1 to 14:1) were studied using design of experiments (DOE) and optimized with canonical analysis. The esterification reaction of oleic acid led to yields of …